| 2015-8-31 |
|
|
CMC-EMagic6 HRC 54 ~ 59 2.6 3.2CMC large mold welding CMC EMagic6 is a highly efficient type blade welding, to achieve the desired low current, high fill rate of melting; after weld metal with excellent toughness and impact resistance, plump and smooth, good adhesion , automatic withdrawal shell, machine processing; suitable for cold steel cladding damage, especially for large stamping die punching site. For the production of cutting tools, the same can by welding on low alloy or ordinary steel production cut edges.
CMC-EMagic10 HRC 55 ~ 58 2.5 3.2
CMC EMagic10 is a W, Cr content higher-efficient blade electrode, to achieve the desired low current, high fill rate of melting; for stamping die blade and high-speed impact of a punch, weld molten gold plump and smooth, good adhesion, automatic withdrawal shell can be machined at high speed hot stamping work environment, but also to maintain the wear resistance; particularly suitable for hardened mold damage repair after surfacing, only one can get a higher hardness. SKD11 quenching molten gold may vary, there is still a high hardness.
CMC-Emagic7 HRC 52 ~ 55 3.2 * 350mm
CMC-Emagic7 as a direct welding on cast iron and cast magical welding electrodes, welding adhesion good, starting from the first layer to have a high hardness, if you pay attention to road between temperature, it will not increase with the welding layers lower hardness; In addition, directly after heat treatment Cr12MoV welded steel, with high hardness performance, special alkaline coating can reduce the stomatal production; can be flat welding, vertical welding, fillet welding, melting of a high fill rate, can accelerate welding efficiency in AC welding fire somewhat less.
CMC-E58 HRC 57 ~ 59 2.4, 3.2, 4.0
Anti-wear, high hardness stability Suitable for cold steel cladding damage, particularly for cold forging die, rolling die, die cutter, automotive stamping dies, metal stamping die bevelled edges. For the production of cutting tools, the same can by welding on low alloy or ordinary steel as the cutting edge. It can also be applied to the hard surface of the wear parts production.
CMC-ECI55 HRC 55-58 3.2 * 350mm
Particularly suitable for deep drawing mold repair and high hardness R angle of drawing parts production. Direct welding cast iron mold GGG70L, FCD, GM241, etc ... Melting fine, with high wear hardness, easy to polish. Genus efficient electrode (melt filling efficiency 120%) of ductile iron, gray cast iron and cast steel flame quenching can also be directly surfacing.
CMC-E46N HRC 45-48 2.4, 3.2
Direct welding on cast iron, for metal stamping die wear is very effective. The first layer of weld metal austenite; from 2 layer begins to martensite abrasion resistance. Flame hardening of cast iron can also be directly surfacing.
CMC-E46H HRC 44-49 3.2 * 350mm
Particularly suitable for chromium molybdenum cast iron mold R angle repair parts and drawing production. Melting fine, easy polishing prevents scratches sheet metal parts; high hardness, suitable for demanding drawbead manufacturing. Ductile iron, gray cast iron and cast steel flame quenching can also be directly surfacing.
CMC-E45 HRC 48 ~ 52 2.6, 3.2, 4.0
Is a better engagement among the hardness of steel rod, suitable for air-cooled steel, cast: as ICD5,7CrSiMnMoV ... and so on. Drawing automobile sheet metal cover mold and large metal sheet metal stamping molds, stretch parts repair can also be used to make stiff dough.
CMC-E64N 3.2 * 350mm
Cast iron welding rod, high strength, good plasticity. Suitable for gray cast iron and ductile iron, machining.
CMC-ENCD HRC 25 ~ 28 3.2 * 350mm
It can be applied directly welded on cast iron, especially for MoCr the welding of cast iron and ductile iron. Is a low-hardness iron-based cast iron electrode, after welding workability, and because the cast iron composition is very close, so no problem of chromatic aberration of the general cast iron welding and after welding heat treatment along with cast iron. Welding performance is good, no holes, cracks.
CMC-E62N 3.2 * 350mm
Especially suitable for cast iron mold, since the amount of nickel-containing reduced, it is possible to reduce the cost, hard surface cast mold production base buffer layer.
CMC-E12HA HRC 57-59 2.4, 3.2, 4.0
Excellent red stripe, widely used in forging, Die, anti-abrasion hard surface production, high hardness stability, for use in forging die, stamping die, die casting, edging cutting die, Cars, hot rolling wheel, hard surface wear parts of the production.
CMC-E60A HRC 60 ~ 62 2.6, 3.2
High hardness stability, resistance to high temperature wear. Suitable for medium carbon steel, low-alloy steel of making hard surface, mechanical wear of the cutting tool repair, car models, forging cold forging die cut welding.
CMC-E30N high tension, high toughness 2.6, 3.2
Engaging high hardness steel, steel seat fixed, hard surface cast mold production base buffer layer of weld cracking.
CMC-E61N 3.2 * 350mm
Adapted, or welding water casting of cast iron, alloy cast iron, steel and cast iron bonded, nickel and alloys.
CMC-E7W (discontinued) HRC 53 ~ 55 3.2, 4.0
Suitable for air-cooled steel (ICD5) or blade production and damage to the surfacing of the cast, especially for the production of automotive sheet metal die cutting edge, punching, flanging parts, light sheet metal stamping die bevelled edges. For the production of cutting tools, the same can be surfacing as a cutting edge. It can also be applied to the hard surface of the wear parts production.
CMC-E47N HRC 44 ~ 50 3.2 * 350mm
Can be directly on the cast iron welding rod, cast iron mold used in the blade, the extension of pressure parts is very convenient.
CMC-EH10 HRC 46 ~ 52 3.2, 4.0
Suitable for medium and large forging die production, repair and resurfacing. Because of the reduced chromium content, and improve the alloy composition of molybdenum, tungsten, vanadium, abrasion and high temperature to form a good balance of toughness, a substantial increase in cross-sectional area larger hot die life. Widely used in the large hot forging dies, forging dies, hot gravity die-casting mold, hard surface wear parts of the production.
CMC-EH13 HRC 55 ~ 58 2.4, 3.2
Suitable for hot-working tool damage resistance welding, especially fervent tools, hot shearing tools, hot planing tools, chamfer edges. For the production of shearing tools, the same can by welding on low alloy or ordinary steel as the cutting edge. |
|